The spherical FeSiAl alloy powder was used as the raw material absorbent, and the flakes were made by extrusion under the action of ball milling to obtain excellent low-frequency adsorbing performance. The phase composition, microstructure and electromagnetic characteristics of the flaky FeSiAl alloy were characterized by X-ray diffraction (XRD), scanning electron microscope (SEM) and vector network analyzer (VNA), the microwave absorption performance was studied. The results indicate that the absorption peaks of FeSiAl alloy absorbent are located in X and Ku bands. The flaky FeSiAl alloy containing 70%(mass fraction) as filler with the thickness of 4.00 mm exhibits strong dielectric and magnetic losses as well as a good impedance matching property. It displays extremely strong electromagnetic wave absorption with reflection loss of –32.8 dB at 2.25 GHz, and the low frequency wave absorbing performance is improved significantly compared with spherical FeSiAl alloy.
Preparation and low-frequency absorbing properties of flaky FeSiAl alloy
2021
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Transportation device for flaky environment-friendly materials
Europäisches Patentamt | 2022
|Process control and mechanical properties of graphene/Al composites based on flaky powder metallurgy
DOAJ | 2021
|Wave-absorbing frequency adjusting method based on wave-absorbing printed circuit
Europäisches Patentamt | 2023
|