In order to study the effect of hole extrusion strengthening process on the fatigue performance of Ti2AlNb alloy, a simulation analysis model of residual stress of hole strengthening process was established. The distribution law of surface residual stress and strengthening mechanism after hole extrusion process were discussed. In this work, the hole extrusion experiments were carried out. The high temperature and low cycle fatigue performance of the compressed and un-compressed specimens were tested respectively. Meanwhile, the microstructure characteristics of the fatigue fracture of the two specimens were compared. The results show that the hole extrusion process can produce a strong residual compressive stress layer around the small hole, which effectively delays and inhibits the initiation and propagation of fatigue cracks, and significantly improves the high temperature and low cycle fatigue performance of Ti2AlNb specimens.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Simulation of residual stress and fatigue test in hole extrusion process for Ti2AlNb alloy


    Beteiligte:
    WANG Yanju (Autor:in) / WANG Xin (Autor:in) / SHA Aixue (Autor:in) / LI Xingwu (Autor:in)


    Erscheinungsdatum :

    2021




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Residual stress test and simulation of incremental hole drilling method

    Wang, Min / Liu, Yunan / Zan, Tao et al. | IEEE | 2016


    Research progress of microstructure transformation and kinetics in Ti2AlNb-based alloy

    CHENG Jianwen / RAO Qunli / LI Jinfu et al. | DOAJ | 2022

    Freier Zugriff

    Cold Expansion Strengthening of 7050 Aluminum Alloy Hole: Structure, Residual Stress, and Fatigue Life

    Qi Li / Qichao Xue / Quansheng Hu et al. | DOAJ | 2022

    Freier Zugriff

    Ti2AlNb/(alpha + beta) Ti double-alloy disc and preparation method thereof

    LI KAI / YANG LIYUAN / LI WEI et al. | Europäisches Patentamt | 2023

    Freier Zugriff