The effects of Sc addition on the microstructure evolution and mechanical properties of X2A66 alloy were studied by the experimental methods of mechanical property test and microstructure characterization. The results indicate that adding 0.18% Sc element in the X2A66 alloy can effectively refine the grain size, and form the primary phase of AlScZr or AlCuScZr with larger size, and also increases the over firing temperature of the as-cast alloy. Compared with Al3Zr particles, Al3(Sc, Zr) composite particles have better effect on restraining recrystallization, and make the alloy have smaller grain size during the subsequent deformation and heat treatment. However, AlCuSc and AlCuScFe phases can not be completely dissolved in the subsequent heat treatment process, which damages the mechanical properties of the solid solution alloy.
Effects of small addition of Sc on microstructure and mechanical properties of X2A66 alloy
2021
Aufsatz (Zeitschrift)
Elektronische Ressource
Unbekannt
Metadata by DOAJ is licensed under CC BY-SA 1.0
Effect of Nd and Y Addition on Microstructure and Mechanical Properties of Extruded Mg-Zn-Zr Alloy
British Library Conference Proceedings | 2007
|Effects of HIP on Microstructure and Mechanical Properties of K4536 Alloy Manufactured by SLM
DOAJ | 2018
|Microstructure and mechanical properties of squeeze cast AZ91D magnesium alloy
Kraftfahrwesen | 2005
|Microstructure and Mechanical Properties of Squeeze Cast AZ91D Magnesium Alloy
SAE Technical Papers | 2005
|Microstructure and Mechanical Properties of Mg-Gd-Sm-Zr Alloy
British Library Conference Proceedings | 2007
|