AZ91 alloy reinforced by carbon nanotubes coated with MgO(AZ91-MgO@CNTs) was prepared by powder metallurgy, hot extrusion and T4 treatment. The influences of MgO@CNTs content and load on the friction and wear property, surface wear morphology and debris topography of AZ91-MgO@CNTs composites were investigated under the dry sliding friction. The results show that MgO@CNTs can improve the wear properties of AZ91-MgO@CNTs. With increasing the content of MgO@CNTs, the strengthening effect of the wear properties of the composite increases and then decreases. Compared with AZ91-CNTs, AZ91-MgO@CNTs has smaller friction coefficient and lower abrasion loss, indicating that the MgO@CNTs is better than CNTs to improve the wear properties of AZ91 alloy. The main wear mechanism of AZ91-MgO@CNTs is abrasive wear under the load of 10 N. When the load is 50 N, there are three wear mechanisms appeared: abrasive wear, oxidation wear and adhesive wear.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Friction and wear properties of AZ91 alloy reinforced by CNTs coated with MgO


    Beteiligte:
    YUAN Qiuhong (Autor:in) / ZHOU Guohua (Autor:in) / LIAO Lin (Autor:in) / WANG Bin (Autor:in) / ZHANG Lei (Autor:in) / XIAO Shan (Autor:in)


    Erscheinungsdatum :

    2023




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Nickel Foam Reinforced AZ91 Magnesium Alloy

    Qiu, K. Q. / Liu, Y. Q. / Suo, Z. Y. et al. | British Library Conference Proceedings | 2007


    Surface Modification of AZ91 Magnesium Alloy

    Luan, B. L. / Gray, J. / Yang, L. X. et al. | British Library Conference Proceedings | 2007




    Eutectic Segregation and Cracking in AZ91 Friction Stir Spot Welds

    Yamamoto, M. / Su, P. / Gerlich, A. et al. | British Library Conference Proceedings | 2007