The microstructure, densification and bending properties of domestic three-dimensional five-directional M55JCf/Al composites at room temperature and 350 ℃ were studied. The results show that the density of domestic three-dimensional five-directional M55JCf/Al composites is 98%, and there are no obvious defects in the microstructure, only a small amount of fiber agglomeration and infiltration micropore defects is existed. The bending strength at room temperature and 350 ℃ is 505 MPa and 335MPa respectively, and the bending modulus is 158 GPa and 138 GPa respectively, showing excellent bending properties at room temperature and high temperature. The research results have a certain role in the development of fiber-reinforced aluminum matrix composites.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Microstructure and bending properties of domestic three-dimensional five-directional M55J Cf/Al composites


    Beteiligte:
    JIN Le (Autor:in) / CAI Changchun (Autor:in) / YU Huan (Autor:in) / XU Zhifeng (Autor:in) / WANG Zhenjun (Autor:in) / LI Yang (Autor:in)


    Erscheinungsdatum :

    2023




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Unbekannt




    Microstructure and mechanical properties of three-dimensional five-directional braided composites

    Li, Dian-sen / Lu, Zi-xing / Chen, Li et al. | Tema Archiv | 2009


    Microstructure and mechanical properties of three dimensional carbon/silicon carbide composites

    Xu, Y. / Zhang, L. / Cheng, L. | British Library Online Contents | 1997


    THREE-DIMENSIONAL DIRECTIONAL OPTICAL ANTENNA

    TANAKA SHINICHI / ISHIHARA HIROSHI | Europäisches Patentamt | 2019

    Freier Zugriff


    Bending of Three-Dimensional Pantographic Column

    Raskin, I. / Roorda, J. / International Union for Theoretical and Applied Mechanics et al. | British Library Conference Proceedings | 2000