OBJECTIVES To evaluate marginal adaptation, fracture load and failure types of CAD/CAM polymeric inlays. METHODS Standardized prepared human molars (48) were divided into four groups (n=12): (A) PCG (positive control group); adhesively luted glass-ceramic inlays, (B) TRX; CAD/CAM polymeric inlays luted using a self-adhesive resin cement, (C) TAC; CAD/CAM polymeric inlays luted using a conventional resin cement, and (D) NCG (negative control group); direct-filled resin-based composite restorations. All specimens were subjected to a chewing simulator. Before and after chewing fatigue, marginal adaptation was assessed at two interfaces: (1) between dental hard tissues and luting cement and (2) between luting cement and restoration. Thereafter, the specimens were loaded and the fracture loads, as well as the failure types, were determined. The data were analysed using three- and one-way ANOVA with post hoc Scheffé test, two sample Student's t-test (p<0.05). RESULTS Before and after chewing fatigue, marginal adaptation for interface 1 showed significantly better results for TRX and PCG than for TAC (p=0.001-0.02) and NCG (p=0.001-0.047). For interface 2, marginal adaptation for TAC was significantly inferior to TRX (p<0.001) and PCG (p<0.001). Chewing fatigue had a negative impact on the marginal adaptation of TAC and NCG. No significant differences in fracture load were found between all tested groups. SIGNIFICANCE Self-adhesive luted polymeric CAD/CAM inlays showed similar marginal adaptation and fracture load values compared to adhesively luted glass-ceramic inlays.


    Zugriff

    Download


    Exportieren, teilen und zitieren



    Titel :

    Marginal adaptation, fracture load and macroscopic failure mode of adhesively luted PMMA-based CAD/CAM inlays


    Beteiligte:
    Ender, Andreas (Autor:in) / Bienz, Stefan (Autor:in) / Mörmann, Werner (Autor:in) / Mehl, Albert (Autor:in) / Attin, Thomas (Autor:in) / Stawarczyk, Bogna (Autor:in)

    Erscheinungsdatum :

    2016-02-01


    Anmerkungen:

    Ender, Andreas; Bienz, Stefan; Mörmann, Werner; Mehl, Albert; Attin, Thomas; Stawarczyk, Bogna (2016). Marginal adaptation, fracture load and macroscopic failure mode of adhesively luted PMMA-based CAD/CAM inlays. Dental Materials, 32(2):e22-e29.



    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch



    Klassifikation :

    DDC:    629 / 796




    Mode I Fracture Testing of Adhesively Bonded Joints

    Klett, Lynn B. / Boeman, Raymond G. | SAE Technical Papers | 1999


    Mode I fracture testing of adhesively bonded joints

    Klett,L.B. / Boeman,R.G. / Oak Ridge National Laboratory,US | Kraftfahrwesen | 1999


    Mode I Fracture Testing of Adhesively Bonded Joints

    Klett, L. B. / Boeman, R. G. / SAE | British Library Conference Proceedings | 1999



    Failure Analysis of Adhesively Bonded Joints

    Sheppard, A. / Kelly, D. / Rose, F. et al. | British Library Conference Proceedings | 1995