Pitting corrosion may have an important influence on the structural integrity of different components used in civil, nuclear, and aerospace engineering because fatigue cracks usually initiate from corrosion pits. It was important to develop a responsible approach to predict the remaining life. An analytical model for the prediction of crack initiation life caused by pits under the interaction of fatigue load and a corrosive environment was proposed in this paper. The effect of the aspect ratio of the pit on the crack initiation life was considered in this model. Compared with the limited experimental data available in the literature, the crack initiation lives predicted by the proposed model agreed well with the experimental data.


    Zugriff

    Zugriff prüfen

    Verfügbarkeit in meiner Bibliothek prüfen

    Bestellung bei Subito €


    Exportieren, teilen und zitieren



    Titel :

    Prediction of Crack Initiation Life due to Corrosion Pits


    Beteiligte:
    Mao, Miaodong (Autor:in) / Zhang, Xiancheng (Autor:in) / Tu, Shantung (Autor:in) / Xuan, Fuzhen (Autor:in)

    Erschienen in:

    Journal of Aircraft ; 51 , 3 ; 805-810


    Erscheinungsdatum :

    2014-02-26


    Format / Umfang :

    6 pages




    Medientyp :

    Aufsatz (Zeitschrift)


    Format :

    Elektronische Ressource


    Sprache :

    Englisch





    Fatigue crack initiation life prediction of railroad wheels

    Liu, Yongming / Stratman, Brant / Mahadevan, Sankaran | Tema Archiv | 2006



    Life Prediction Algorithms for Aero Engine Discs Based on Crack Initiation and Crack Propagation Models

    Dhondt, G. / Commission of the European Communities | British Library Conference Proceedings | 1993